Bambu Lab Silk PLA Spool 1.75mm - 1kg

Bambu PLA Silk
Bambu PLA Silk offers a silk-like and high-glossy that adds a luxury appearance to your prints while retaining PLA's ease of use. Different with other silk filaments, Bambu PLA Silk was toughened and demonstrates greater resistance to breakage when using AMS printing. It's ideal for decorations, artistic projects, and 3D character models or any parts where you want it shinier.

Silk-like appearance with ultra-high gloss
Bambu PLA Silk brings a silk-like appearance and long-lasting high gloss to your 3D prints, transforming models into stunning art.

Display of Silk Prints
Bambu PLA Silk is ideal for decorations, artistic projects, and 3D character models or any parts where you want it shinier.

Enhanced Toughness & AMS Compatible
Compared with regular PLA Silk, Bambu PLA Silk was toughened and demonstrates greater resistance to breakage when using AMS printing.

Controllable gloss
The appearance gloss of the model printed by Silk material can be controlled by printing temperature and speed. To get glossier finishes, higher printing temperatures and/or lower speeds are recommended.

RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.

Accessory Compatibility

• Build Plate: Cool Plate, High Temperature Plate or Textured PEI Plate
• Hotend: Hotend with Hardened Steel Nozzle (0.4mm) / Hotend with Stainless Steel Nozzle (0.2mm, 0.4mm)
• Glue: Liquid Glue / Glue Stick
• Not Recommended: Engineering Plate, Hotend with Hardened Steel Nozzle (0.6mm, 0.8mm)

Recommended Printing Setting

Drying Settings (Blast Drying Oven)	55 °C，8 h
Printing and Keeping Container's Humidity	< 20% RH (Sealed, with Desiccant)
Nozzle Temperature	210 - 240 °C
Bed Temperature (with Glue)	35 - 45 °C
Printing Speed	< 250 mm/s

Physical Properties

Density	1.32 g/cm³
Vicar Softening Temperature	56 °C
Heat Deflection Temperature	53 °C
Melting Temperature	152 °C
Melt Index	20.5 ± 1.2 g/10 min

Mechanical Properties

Tensile Strength	27 ± 4 MPa
Breaking Elongation Rate	3.5 ± 0.6 %
Bending Modulus	2370 ± 150 MPa
Bending Strength	66 ± 4 MPa
Impact Strength	24.5 ± 1.7 kJ/m²