Bambu Lab Polycarbonate Spool 1.75mm - 1kg
Only %1 left
Exceptional Thermal Resistance
Excellent Mechanical Properties
High Impact Strength and Durability
Suitable for Engineering Purpose
Comes with High Temperature Reusable Spool
Diameter: 1.75mm +/- 0.03mm
Excellent Mechanical Properties
High Impact Strength and Durability
Suitable for Engineering Purpose
Comes with High Temperature Reusable Spool
Diameter: 1.75mm +/- 0.03mm
Accessory Compatibility
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.
Cautions for Use
1. Due to the transparent properties of the filament, Lidar Extrusion Calibration can be affected when printing Transparent PC.
2. Bambu PC needs proper drying before printing, recommended drying temperature is 80 ℃ for 8 hours in a blast drying oven, or 100 ℃ for 12 hours on a printer's heatbed.
Recommended Printing Settings
Physical Properties
Mechanical Properties
- Build Plate: Engineering Plate, High Temperature Plate or Textured PEI Plate
- Not Recommended: Cool Plate
- Hotend: All Size / Material
- Glue: Glue Stick (Bambu Liquid Glue not recommended)
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.
Cautions for Use
- Dry out before use
- AMS Compatible
- Enclosure Printers Required
1. Due to the transparent properties of the filament, Lidar Extrusion Calibration can be affected when printing Transparent PC.
2. Bambu PC needs proper drying before printing, recommended drying temperature is 80 ℃ for 8 hours in a blast drying oven, or 100 ℃ for 12 hours on a printer's heatbed.
Recommended Printing Settings
Drying Settings (Blast Drying Oven) | 80 °C,8h |
Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
Nozzle Temperature | 260 - 280 °C |
Bed Temperature (with Glue) | 90 - 110 °C |
Printing Speed | < 300 mm/s |
Physical Properties
Density | 1.20 g/cm³ |
Vicar Softening Temperature | 119 °C |
Heat Deflection Temperature | 117 °C |
Melting Temperature | 228 °C |
Melt Index | 32.2 ± 2.9 g/10 min |
Mechanical Properties
Tensile Strength | 55 ± 4 MPa |
Breaking Elongation Rate | 3.8 ± 0.3 % |
Bending Modulus | 2310 ± 70 MPa |
Bending Strength | 108 ± 4 MPa |
Impact Strength | 34.8 ± 2.1 kJ/m² |