Bambu Lab PETG-CF Spool 1.75mm - 1kg
Premium Print Surface
Improved Mechanical Properties & High Flexibility
Comes with Basic Reusable Spool
Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- Recommended to Dry Out Before Use
- AMS Compatible
- 0.2 mm Nozzle Not Compatible
Bambu PETG-CF
Bambu PETG-CF is a composite material consisting of PETG and carbon fiber. The new formula greatly improved printing quality by reducing nozzle clogging and clumping compared to traditional PETG. With the addition of carbon fiber, Bambu PETG-CF offers improved strength while maintaining good toughness and a shiny look. It is an ideal material for drone parts, racing models, and various functional parts that require both high performance, especially impact strength, and a sleek appearance.
Less clumping and stringing
Bambu PETG-CF is improved with a modified formula that specifically addresses the issue of clumping and sticking to nozzle during PETG printing.
Premium print surface
Carbon fiber brings advanced texture to the print surface, while retaining the shine of PETG itself.
High Flexibility
Compared to other carbon fiber materials, Bambu PETG-CF exhibits exceptional toughness and is less prone to fracture under external stress and impact.
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
Bambu PETG-CF needs proper drying before printing. Recommended drying condition is 65 ℃ for 8 hours in a blast drying oven, and 75 ℃ for 12 hours on a printer‘s heatbed. Learn more about filament drying. Please refer to: Filament drying cover on WIKI.
To get stronger Z-adhesion, please set a higher infill density, and do not use an open-frame printer or set too large fan percentages to avoid over cooling.
To get shinier looks, set lower speeds and relatively higher temperatures.
Recommended Print Settings
Drying Settings (Blast Drying Oven) | 65 °C,8 h |
Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
Nozzle Temperature | 240 - 270 °C |
Bed Temperature (with Glue) | 65 - 75 °C |
Printing Speed | < 200 mm/s |
Physical Properties
Density | 1.25 g/cm³ |
Vicar Softening Temperature | 85 °C |
Heat Deflection Temperature | 74 °C |
Melting Temperature | 225 °C |
Melt Index | 19.3 ± 2.4 g/10 min |
Mechanical Properties
Tensile Strength | 35 ± 5 MPa |
Breaking Elongation Rate | 10.4 ± 0.6 % |
Bending Modulus 2910 | ± 260 MPa |
Bending Strength | 70 ± 5 MPa |
Impact Strength | 41.2 ± 2.6 kJ/m² |
PETG-CF Hex Code Table
Brick Red | #9F332A |
Violet Purple | #583061 |
Indigo Blue | #324585 |
Malachite Green | #16B08E |
Black | #000000 |
Titan Gray | #565656 |